Product Details:
Payment & Shipping Terms:
|
| Standard: | Malaysia | Woven: | Unidirectional |
|---|---|---|---|
| Tensile Strength: | 3400Mpa | Anti High Temperature: | Yes |
| Specs: | High Strength | Materials: | Carbon Fiber CFRP Fabric |
| High Light: | cfrp composite material,carbon fiber fabric roll |
||
300gsm Malaysian Standard Carbon fiber CFRP fabric with high strength
Weight: 300gsm
Density: 1.8g/cm³
Packing: 100 meters/roll
Width: 100mm, 200mm, 300mm, 500mm or to be customized.
Storage Condition:Store dry at 40°-95° F(4° -35°)
Shelf Life: 50 years
Color:Black
Carbon Fiber Type: 0° (unidirectional)
300gsm Malaysian Standard Carbon fiber CFRP fabric with high strength
CFRP fabric strengthening of existing structures can involve complex evaluation, design, and detailing processes, requiring a good understanding of the existing structural conditions along with the materials used to repair the structure prior to CFRP fabric installation. The suitability of FRP for a strengthening project can be determined by understanding what FRP is and the advantages it offers, but more importantly, its limitations.
A mix of usually carbon fibre cfrp fabrics, and an epoxy resin, wrapping systems are custom designed for each project and application. Where there is an element of corrosion in the structure, carbon fibre wrapping can be used to both weather-proof corrosion and structurally re-enforce the structure. The impervious material will protect a structure from moisture intrusion and further corrosion, reducing the need for ongoing maintenance work.
Advantages
Used for shear, confinement, seismic or flexural strengthening
Versatile, can be wrapped around complex geometries
High Strength
Light Weight
Non-corrosive
Alkali Resistant
Low aesthetic impact
|
Testing project |
Standard |
|
High Strength Grade 1 |
|
|
Tensile strength |
≥3400 MPa |
|
Tensile modulus of elasticity |
≥2.3×105 MPa |
|
Elongation |
≥1.6 % |
|
Bending Strength |
≥700 MPa |
|
Layer cutting strength |
≥45 MPa |
|
Cohesive pulling strength with base materials
|
To concrete and brick materials, ≥2.5 MPa
|
|
Thickness |
0.167mm |
Application
Basements Driveways
Patios Pools
Small Industrial Parking Garages
Buildings Bridges Piers/Wharfs Tunnels
Roads Sidewalks Stadiums Shopping Malls
Schools Dams Tanks/Silos Pipes
Blast Reinforcement
Military
How to Use CFRP Fabric
• Surface treatment
• Applying primer
• Leveling
• Applying carbon fiber adhesive
• Externally bonded carbon fiber reinforced polymer(CFRP) fabric
• Applying carbon fiber adhesive again
• Curing and protecting
Preparation works
Surface must be clean and sound. It may be dry or damp, but free of standing water and frost. Remove dust, laitance, grease, curing compounds, impregnations, waxes, foreign particles, disintegrated materials and other bond inhibiting materials from the surface. Existing uneven surfaces must be filled with an appropriate repair mortar. The adhesive strength of the concrete must be verified after surface preparation by random pull-off testing (ASTM D 4541) at the discretion of the engineer. Minimum tensile strength required is 200 psi (1.4 MPa) with concrete substrate failure (typical).