|Materials:||Carbon Fiber||Tensile Strength:||3400Mpa|
carbon epoxy laminate,
plain weave carbon fiber
XQ Carbon Fiber Strip
Applied for tension, shearing and seismic reinforcement of section units, this product can be used together with impregnated adhesive as carbon fiber composite materials to make an enhanced system of high performance carbon fiber cloth and sheet. Suitable for increasing the working load of building, changing the using function of project, materials ageing, concrete strength grade below design value, structure crack treatment, repairing of section unit under bad condition, reinforcement of protecting facility.
Range of Application:
Reinforcement for unplanted steel bar
Anti-seismic reinforcement for additional layer
Maintenance and reinforcement for viaduct and bridge
New door reinforcement for shear wall
Reinforcement and repairing for all kinds of structure and section units.
Specially suitable for reinforcement of complicated structures as curved surface and joint.
1, high strength, low density and thickness, no increasing the weight and size of reinforced section unit
2, Widely used for repairing,seismic strengthening and reinforcement of building,bridges,tunnels and other structures,
3, Easy to handle, no need for large equipment, no wet, no fire, no fixed installations;
4, suitable for acids, alkalis, salts and atmospheric corrosion environments;
5, Suitable for reinforcement and seismic reinforcement of concrete, bricks,wooden structures in port, water conservancy and hydropower project, especially complicated structures as curved surface and joints.
Base concrete materials strength must be above C15, temperature range 5-35℃, relative humidity no more than 70%.
1. Basic parameters
1) Specification: 200g/㎡
2) Appearance: black woven fabric
3) Weave: unidirectional;
4) Strength class: high strength Grade I, Grade II
5) Length: 50 m, 100 m
6) Width: 100mm, 200mm, 300mm, 500mm, other sizes can be customized
|High Strength Grade I|
|Tensile strength||≥3400 MPa|
|Tensile modulus of elasticity||≥2.3×105 MPa|
|Bending Strength||≥700 MPa|
|Layer cutting strength||≥45 MPa|
Cohesive pulling strength with base materials
To concrete and brick materials, ≥2.5 MPa
Remarks: all data are average values.
unloading→ Base layer treatment → glue resin on base layer → leveling → paste Carbon fiber sheet ( please pay attention for safety as the carbon fabric is conductive → Inspection → Surface protecting and decoration.
1, carbon fabric cloth is conductive, please leave far away from electrical equipment and power supply, or take reliable protection
2, carbon cloth bent should be avoided in the process
3, the surface should be clean and dry;
4, temperature theoretically should be 5-40 ℃
5, Processing in rain and outdoor is prohibited
6, If relative humidity is greater than 85% or condensation on the concrete surface, Processing is not allowed;
7, Matched resin shall be stored sealed and away from fire and direct sunlight.
8, The place of the formulation and use of resins should maintain good ventilation;
9, on-site workers should take appropriate protection measures.
1. Material quality
many suppliers use basalt fiber, aramid fiber contracted black to posing as carbon fiber cloth, this will caused project quality unqualified, so firstly need to know that the carbon fiber has black and bright tows, it will not curl but red as steel wire after burning, smooth, glossy, well-distributed,and with good conductive performance
2, Bonding quality
strictly abide with <<processing and inspection standard for carbon fiber>> Ensuring the quality of bonding quality;
3, carbon fiber has good tensile strength, but is poor for fold and bending
4, carbon fiber cloth shall be covered with anti-corrosion mortars after processing, long time exposure will reduce its service life.
Contact Person: Colin Mao