Product Details:
Payment & Shipping Terms:
|
| Tensile Strength: | Above 30Mpa | Tensile Modulus Of Elasticity: | ≥3200 MPa |
|---|---|---|---|
| Mixing Ratio: | 3:1 | Bending Strength: | ≥30 MPa |
| Color: | Grey | Application: | Concrete Crack Seal |
| High Light: | polyurethane concrete crack sealant,concrete leak sealer |
||
Xq-FF32 2-Component Structural Epoxy Bonding Agent
Concrete Crack Repairing Grout Epoxy
Crack Repair Grouting adhesive
Xq-FF32 2-Component Structural Epoxy Bonding Agent is a structural, moisture tolerant, two part bonding agent, based on a combination of epoxy resins and special fillers, designed for use at temperatures between +10°C and +30°C.
Features and Benefits
Easy to mix and apply
Suitable for dry and damp concrete surfaces
Very good adhesion to most construction materials
High Bond Strength
Hardens without shrinkage
Different coloured components (for mixing control)
No primer needed
High initial and ultimate mechanical strength
Impermeable to liquids and water vapour
Good chemical resistance
As a structural bonding agent and adhesive for:
Concrete elements (including bonding fresh to hardened concrete)
Hard natural stone
Ceramics, fibre-cement
Mortar, Bricks, Masonry
Steel, Iron, Aluminium
Wood
Polyester / fibreglass and Epoxy resin materials
Glass
Easy to mix and apply
Suitable for dry and damp concrete surfaces
Very good adhesion to most construction materials
High Bond Strength
Hardens without shrinkage
Different coloured components (for mixing control)
No primer needed
High initial and ultimate mechanical strength
Impermeable to liquids and water vapour
Good chemical resistance
CHARACTERISTICS / ADVANTAGES
▪ Easy to mix and apply
▪ Suitable for dry and damp concrete surfaces
▪ Very good adhesion to most construction materials
▪ High bond strength
▪ Hardens without shrinkage
▪ Different coloured components (for mixing control)
▪ No primer needed
▪ High initial and ultimate mechanical strength
▪ Impermeable to liquids and water vapour
▪ Good chemical resistance
| Testing project | Standard | Result |
| Gel Performance according to GB50728-2011 standard | ||
| Tensile Strength (MPa) | ≥30 Mpa | 33.8 Mpa |
| Tensile modulus of elasticity (MPa) | ≥3200 Mpa | 4194 Mpa |
| Elongation | ≥1.2 % | 1.27 % |
| Bending Strength (MPa) |
≥45 Mpa (no fragment damage) |
55.2 Mpa |
| Compressive Strength (MPa) | ≥65 | 73.2 Mpa |
| Bonding Capacity according to GB50728-2011 standard | ||
| Steel-Steel Tensile Shear Strength (MPa) | ≥15 Mpa | 18.0 Mpa |
| Steel-Steel bonding tensile strength (MPa) | ≥33 Mpa | 34.7 Mpa |
| Steel-Steel T-peeling strength (MPa) | ≤25mm | 13.7mm |
| Steel to C45 Concrete cohesive pulling strength (MPa) |
≥2.5 Mpa (Concrete cohesion damage) |
3.3 Mpa |
| Heat transform temperature | ≥65 ℃ | 68.4 ℃ |
| Non-volatile content | ≥99 % |
99.5 %
|
Processing Flow:
Crack marking
Surface treatment
Embedding the injector
Sealing with adhesive
Sealing inspection
Mixing crack grouting adhesive
Low pressure injection
Hardening
Inspection
Packaging and Logistics
1. Two components packed separately, the mixing ratio is 3:1
2. Shall be stored in cool (under 25℃), dry and ventilated place, no exceed 2 year.
3. This product is non dangerous goods, can be shipped as normal chemical materials.
Attention
Shall be stored in cool, dry and ventilated place, avoid sun exposure and high temperature
If touched by skin, clean with acetone and washed by water immediately
Do not mix too much at each time, use upon actual necessary