Product Details:
Payment & Shipping Terms:
|
| Tensile Strength: | Above 30Mpa | Tensile Modulus Of Elasticity: | ≥3200 MPa |
|---|---|---|---|
| Mixing Ratio: | 3:1 | Bending Strength: | ≥30 MPa |
| Color: | Grey | Application: | Concrete Crack Seal |
| High Light: | polyurethane concrete crack sealant,concrete leak sealer |
||
High Strength Epoxy Concrete Crack Sealer For Building Retrofitting
Concrete Crack Repairing Grout Epoxy
Crack Repair Grouting adhesive
High Strength Epoxy Concrete Crack Sealer For Building Retrofitting
Features with high hardness, excellent Polish, strong adhesion, fast curing, easy to bond with the substrate such as concrete, stone, steel. Is a modified epoxy, initial adhesiveness.
Range of Application
Assorted with XQ-GF crack grouting adhesive when repairing concrete cracks,
Mainly used for crack sealing and base bonding during processing of repairing the concrete crack and grouting.
Sealing around the steel plate during steel wrap process
Repairing and leveling for the concrete surface.
Used for steel bar planting at secondary structure part.
Features
1, Low temperature or room temperature curing, fast curing speed;
2, Modified epoxy resin, good initial adhesiveness;
3, high adhesive strength after curing, good hardness and a certain toughness;
4, Good anti-acid after curing, good performance against moisture water, oil, dust,humidity and weather ageing
5, The cured products have good strength for tension, pressure and bonding
Product performance
Basic parameters
1) Appearance
Part A (main): Grey Gel
Part B (hardener): Beige Gel
2) Mixing ratio (weight): 3:1
3) Handling time (25℃): ≥30min
4) Hardening time: 3 hours
5) Shelf time: 24 months
Product Performance
1 Main Performance
| Testing project | Standard | Result |
| Gel Performance according to GB50728-2011 standard | ||
| Tensile Strength (MPa) | ≥30 Mpa | 33.8 Mpa |
| Tensile modulus of elasticity (MPa) | ≥3200 Mpa | 4194 Mpa |
| Elongation | ≥1.2 % | 1.27 % |
| Bending Strength (MPa) |
≥45 Mpa (no fragment damage) |
55.2 Mpa |
| Compressive Strength (MPa) | ≥65 | 73.2 Mpa |
| Bonding Capacity according to GB50728-2011 standard | ||
| Steel-Steel Tensile Shear Strength (MPa) | ≥15 Mpa | 18.0 Mpa |
| Steel-Steel bonding tensile strength (MPa) | ≥33 Mpa | 34.7 Mpa |
| Steel-Steel T-peeling strength (MPa) | ≤25mm | 13.7mm |
| Steel to C45 Concrete cohesive pulling strength (MPa) |
≥2.5 Mpa (Concrete cohesion damage) |
3.3 Mpa |
| Heat transform temperature | ≥65 ℃ | 68.4 ℃ |
| Non-volatile content | ≥99 % |
99.5 %
|
Processing Flow:
Crack marking
Surface treatment
Embedding the injector
Sealing with adhesive
Sealing inspection
Mixing crack grouting adhesive
Low pressure injection
Hardening
Inspection
Packaging and Logistics
1. Two components packed separately, the mixing ratio is 3:1
2. Shall be stored in cool (under 25℃), dry and ventilated place, no exceed 2 year.
3. This product is non dangerous goods, can be shipped as normal chemical materials.
Attention
Shall be stored in cool, dry and ventilated place, avoid sun exposure and high temperature
If touched by skin, clean with acetone and washed by water immediately
Do not mix too much at each time, use upon actual necessary