Building Carbon Fiber Adhesive >3mm Thixotropy Index Strong Penetration Ability

Building Carbon Fiber Adhesive >3mm Thixotropy Index Strong Penetration Ability

Building Carbon Fiber Adhesive >3mm Thixotropy Index Strong Penetration Ability
Building Carbon Fiber Adhesive >3mm Thixotropy Index Strong Penetration Ability

Large Image :  Building Carbon Fiber Adhesive >3mm Thixotropy Index Strong Penetration Ability

Product Details:
Place of Origin: China
Brand Name: XINCHOR
Certification: CE
Model Number: XQ-XW21C
Payment & Shipping Terms:
Minimum Order Quantity: 100 kgs
Price: Negotiable
Packaging Details: 100 meters per roll in carton
Delivery Time: 30 days
Detailed Product Description
Materials: Epoxy Resin Thixotropy Index: >3mm
Resistance To Freezing And Thawing: Reduction Rate Of Shearing Strength ≤5% Packing: Barrel Or Plastic Bucket
CE Approved: Yes Shelf Life: 2 Years
High Light:

epoxy resin adhesive

,

two part epoxy

Structural Strengthening Carbon Fiber Adhesive With High Tensile Strength

Carbon Fiber Primer

Carbon Fiber Leveling Adhesive

Carbon Fiber Reinforced Polymer

 

Structural Strengthening Carbon Fiber Adhesive With High Tensile Strength

Xinchor CFRP Carbon Fiber Adhesive is Low viscosity, strong penetration ability, used for smearing of the underlayer of reinforced members' surface, the role is penetration bonding reinforcement to the broken concrete after chiseling off; of the surface of members was intact, smearing was not needed.

 

Application Range

Load increases

Seismic reinforcement

Improve structural state

Damage of structural parts

Change the structural function

Remit mistakes in design and construction

 

Flexural strengthening,

Shear strengthening,

Column confinement and ductility improvement.

 

Load Increases

Increased live loads

Increased traffic volumes on bridges

Installation of heavy machinery in industrial buildings

Vibrating structures

Changes of building utilization

Seismic Strengthening

Column wrapping

Masonry walls

Damage to Structural Parts

Aging of construction materials

Vehicle impact

Fire

Blast resistance

 

Testing project Standard Result
  Lot#1 Lot#2 Lot#3
Tensile Strength ≥38 Mpa 46.7 48.6 47.6
Tensile modulus of elasticity ≥2400 MPa 2437 2484 2473
Elongation ≥1.5% 2.79 2.80 2.63
Bending Strength

≥50Mpa

(no fragmental damage)

91.0 88.8 84.9
Compressive Strength ≥70 Mpa 77.6 83.0 81.5
Bonding Capacity    
Steel-Steel Tensile Shear Strength (23±2), (50±5)%RH ≥14 Mpa 14.3 14.9 14.2
Steel-Steel bonding tensile strength ≥40 Mpa 40.7 40.1 41.1
Steel-Steel T-impact peeling strength 20 mm 0 0 0
Steel to C45 Concrete cohesive haul strength ≥2.5 Mpa (Concrete cohesion damage) 4.5 4.2 4.4
Thermal deformation temperature ≥65 65.8 66.1 66.4
Non-volatile content ≥99% 99.5 99.5 99.5
Thixotropy Index ≥3mm 3.3 3.2 3.2
Ageing resistance to heat and humidity Reduction rate of shearing strength ≤12% 11.6 11.2 10.5
Ageing resistance to heat Reduction rate of shearing strength ≤5% 3.9 4.7 4.0
Resistance to alkaline medium No reduction of strength and only destruction of concrete. without any cracks, stripping, foaming on appearance pass pass pass
Resistance to alkaline medium No reduction of strength and only destruction of concrete. without any cracks, stripping, foaming on appearance pass pass pass
Resistance to freezing and thawing Reduction rate of shearing strength ≤5% 2.9 3.4 3.5
Resistance to long term stress No defect after steel to steel shearing, The deformation value of creep <0.4mm 0.2 0.1 0.2
Resistance to salt spray Reduction rate of shearing strength ≤5% 4.1 4.5 4.1

 

 

 

Building Carbon Fiber Adhesive >3mm Thixotropy Index Strong Penetration Ability 0

 

 

 

Contact Details
ZHEJIANG XINCHOR TECHNOLOGY CO., LTD.

Contact Person: Colin Mao

Tel: 86-13336183725

Send your inquiry directly to us (0 / 3000)