XQ-FF31 Concrete Crack Sealer , Polyurethane Concrete Crack Sealant Fast Curing

XQ-FF31 Concrete Crack Sealer , Polyurethane Concrete Crack Sealant Fast Curing

XQ-FF31 Concrete Crack Sealer , Polyurethane Concrete Crack Sealant Fast Curing
XQ-FF31 Concrete Crack Sealer , Polyurethane Concrete Crack Sealant Fast Curing

Large Image :  XQ-FF31 Concrete Crack Sealer , Polyurethane Concrete Crack Sealant Fast Curing

Product Details:
Place of Origin: China
Brand Name: XINCHOR
Model Number: XQ-FF31
Payment & Shipping Terms:
Minimum Order Quantity: 100 kgs
Price: Negotiable
Packaging Details: 100 meters per roll in carton
Delivery Time: 30 days
Detailed Product Description
Tensile Strength: Above 30Mpa Tensile Modulus Of Elasticity: ≥3200 MPa
Mixing Ratio: 3:1 Bending Strength: ≥30 MPa
Color: Grey Application: Concrete Crack Seal
High Light:

concrete gap sealer

,

concrete leak sealer

XQ-FF31 Hi-Mod Gel High-modulus, high-strength, structural, epoxy paste adhesive

Concrete Crack Repairing Grout Epoxy

Crack Repair Grouting adhesive

 

XQ-FF31 Hi-Mod Gel High-modulus, high-strength, structural, epoxy paste adhesive

Features with high hardness, excellent Polish, strong adhesion, fast curing, easy to bond with the substrate such as concrete, stone, steel. Is a modified epoxy, initial adhesiveness.

 

Usage
Structural bonding of concrete, masonry, metals, wood, etc. to a maximum glue line of 1⁄8 in. (3 mm).
Grout bolts, dowels, and pins.
Seals cracks and around injection ports prior to pressure-injection grouting.
Interior, vertical, and overhead repair of concrete as an epoxy mortar binder.
As a pick-proof sealant around windows, doors, lock-ups etc. inside correctional facilities.

 

Advantages
Meets physical requirements of China National Standard.
Excellent adhesion to concrete, masonry, metals, wood, and most structural materials.
Paste consistency ideal for vertical and overhead repair of concrete.
Fast-setting and strength-producing adhesive.
Convenient easy mix ratio A:B = 3:1 by volume.

 

Product performance

 

Basic parameters

1) Appearance

Part A (main): Grey Gel

Part B (hardener): Beige Gel

2) Mixing ratio (weight): 3:1

3) Handling time (25℃): ≥30min

4) Hardening time: 3 hours

5) Shelf time: 24 months

 

Product Performance

1 Main Performance

 

Testing project Standard Result
Gel Performance according to GB50728-2011 standard  
Tensile Strength (MPa) ≥30 Mpa 33.8 Mpa
Tensile modulus of elasticity (MPa) ≥3200 Mpa 4194 Mpa
Elongation ≥1.2 % 1.27 %
Bending Strength (MPa)

≥45 Mpa

(no fragment damage)

55.2 Mpa
Compressive Strength (MPa) ≥65 73.2 Mpa
Bonding Capacity according to GB50728-2011 standard
Steel-Steel Tensile Shear Strength (MPa) ≥15 Mpa 18.0 Mpa
Steel-Steel bonding tensile strength (MPa) ≥33 Mpa 34.7 Mpa
Steel-Steel T-peeling strength (MPa) ≤25mm 13.7mm
Steel to C45 Concrete cohesive pulling strength (MPa)

≥2.5 Mpa

(Concrete cohesion damage)

3.3 Mpa
Heat transform temperature ≥65 68.4 ℃
Non-volatile content ≥99 %

99.5 %

 

 

Processing Flow:

Crack marking

Surface treatment

Embedding the injector

Sealing with adhesive

Sealing inspection

Mixing crack grouting adhesive

Low pressure injection

Hardening

Inspection

 

 

Packaging and Logistics

1. Two components packed separately, the mixing ratio is 3:1

2. Shall be stored in cool (under 25℃), dry and ventilated place, no exceed 2 year.

3. This product is non dangerous goods, can be shipped as normal chemical materials.

 

Attention

Shall be stored in cool, dry and ventilated place, avoid sun exposure and high temperature

If touched by skin, clean with acetone and washed by water immediately

Do not mix too much at each time, use upon actual necessary

 

XQ-FF31 Concrete Crack Sealer , Polyurethane Concrete Crack Sealant Fast Curing 0

Contact Details
ZHEJIANG XINCHOR TECHNOLOGY CO., LTD.

Contact Person: Colin Mao

Tel: 86-13336183725

Send your inquiry directly to us (0 / 3000)